M. A. Soleimani, R. Naghizadeh, A. R. Mirhabibi, F. Golestanifard. EFFECT OF CALCINATION TEMPERATURE OF THE KAOLIN AND MOLAR Na2O/SiO2 ACTIVATOR RATIO ON PHYSICAL AND MICROSTRUCTURAL PROPERTIES OF METAKAOLIN BASED GEOPOLYMERS. IJMSE 2012; 9 (4) :43-51
URL: http://ijmse.iust.ac.ir/article-1-504-en.html
EFFECT OF CALCINATION TEMPERATURE OF THE KAOLIN AND MOLAR Na2O/SiO2 ACTIVATOR RATIO ON PHYSICAL AND MICROSTRUCTURAL PROPERTIES OF METAKAOLIN BASED GEOPOLYMERS
M. A. Soleimani , R. Naghizadeh , A. R. Mirhabibi , F. Golestanifard
Abstract:   (22728 Views)
Metakaolinite-based geopolymer has been synthesized at about 25 °C from metakaolin which has been calcined in different temperatures (600-900 °C) and different Na2O/SiO2 ratio activator (0.3-1.1). Compressive strength and microstructure of cement pastes after 7-28 days curing at ambient temperature were measured. Compressive strength tests on the samples showed that the sample made with calcined kaolin at 700 °C and molar ratio of 0.6 has highest average compressive strength of 32 MPa after 28 days of curing. Evaluation of infrared spectroscopy (FTIR) and microstructure showed that geopolymer cement developed and new molecular structure established
Keywords: Geopolymer, Metakaolin, Compressive strength, Activator
Full-Text [PDF 653 kb]   (9315 Downloads)    
Type of Study: Research Paper |
Add your comments about this article : Your username or Email:
CAPTCHA
Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb