Abstract:

activity gas diffusion process has been investigated in this research. Effects of coating temperature and aluminum

concentration in powder mixture on formation mechanism were studied using optical and scanning electron

microscopes, EDS and X-ray diffraction (XRD) techniques. For this purpose two different packs containing 1 and 2

wt% aluminum powder, were used for coating the samples at two temperatures, 850ºC and 1050ºC. The ratio of Al to

activator was kept constant in both packs. By increasing the Al content in high activity powder mixture, the

concentration of diffused Al increased in the coating layers, and the thickness of coating increased. At 1050ºC as the

rate of diffused Al to the interdiffusion zone increased, this zone gradually transformed to outer coating phases. At

850ºC coating formed by inward diffusion of Al, but at 1050ºC it was initially formed by inward diffusion of Al followed

by outward diffusion of Ni.