R. Khoshhal, M. Soltanieh, M. Mirjalili. FORMATION AND GROWTH OF TITANIUM ALUMINIDE LAYER AT THE SURFACE OF TITANIUM SHEETS IMMERSED IN MOLTEN ALUMINUM. IJMSE 2010; 7 (1) :24-31
URL: http://ijmse.iust.ac.ir/article-1-250-en.html
Abstract:   (37998 Views)

Abstract:

titanium sheets in pure molten aluminum at 750

and X-Ray Diffraction Analysis results, TiAl

intermetallic layer thickness increases slowly at primary stages. After that an enhanced growth rate occurs due to layer

cracking and disruption. Presumably, reaction starts with solving titanium into the molten aluminum causing in

titanium super saturation and TiAl

intermetallic layer which consequently leads to TiAl

energy of intermetallic layer formation and growth was developed by measuring titanium thickness decreases.

In this work, kinetics of intermetallic compounds formation in Al-Ti system was studied by immersingoC, 850 oC and 950 oC. According to Scanning Electron Microscopy3 is the only phase can form at the interface. Observations revealed that3 formation. At this stage, growth may be controlled by aluminum diffusion through3 formation at the interface of Ti-TiAl3. Furthermore, activation
Full-Text [PDF 2855 kb]   (8778 Downloads)    
Type of Study: Research Paper |

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb